The Effect of Circulation of 3% HCL Solution On the Corrosion Rate of Aluminum
DOI:
https://doi.org/10.21063/jtm.2020.v10.i2.114-117Kata Kunci:
Corrosion, corrosion rate, circulation, aluminum, HClAbstrak
Corrosion is usually called rusting. Corrosion to aluminum is carried out by circulating and non-circulating methods. The specimens were placed in 3% HCl solution, each with 3 specimens in one vessel. There are 9 specimens in 3 vessels. In this study, aluminum was immersed with a circulation of 385 L/hour and 432 L/hour and also without circulation with immersion time for 4 days. The highest corrosion rate was obtained in aluminum soaked in 3% HCl for 4 days with a circulation of 432 L / hour, 0.5215 Mpy. The lowest corrosion rate was obtained for aluminum immersed in 3% HCl for 4 days without circulation, 0.1830 Mpy.
Referensi
. M. G. Fontana, (1987). Teori Dasar Korosi.
. A. K. Sari, (2017). Studi Karakteristik Laju Korosi Logam Aulminium Dan Pelapisan Dengan Menggunakan Membran Sellulosa Asetat, 6(1), 36–40.
. ASM Handbook, (2003), Properties and Selection: Irons, steels and high performance alloys.
. A. Ngatin, Y. Tonapa dan R.A.K. Regiyanti, (2017). Prosiding Seminar Nasional Kimia UNY 2017 Sinergi Penelitian dan Pembelajaran untuk Mendukung Pengembangan Literasi Kimia pada Era Global Ruang Seminar FMIPA UNY, 14 Oktober 2017, 269–278.
. A.A. Hakim, 2011. Pengaruh Inhibitor Korosi Berbasiskan Sunyawa Fenolik untuk Proteksi Pipa Baja Karbon pada Lingkungan 0.5, 1.5, 2.5, 3.5% NaCl yang Mengandung Gas CO2. Skripsi. Depok: Teknik Material dan Metalurgi, Fakultas Teknik Universitas Indonesia.
. W.D. Callister, Material Science And Engineering An Introduction, Jhon Wiley & Sons, Inc., Singapore, 2004.
Unduhan
Diterbitkan
Terbitan
Bagian
Lisensi
Hak Cipta (c) 2020 I.E. Putra
Artikel ini berlisensiCreative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.