Strength Analysis of Betelnut Fiber-Reinforced Resin Composite
DOI:
https://doi.org/10.21063/jtm.2016.v6.i2.87-92Kata Kunci:
composite, betelnutfiber, epoxy, fiber orientation, tensile strenghtAbstrak
Material is needed in life, the material itself is used aims to facilitate human activities, in the development of modified human material in various ways, one of which composite materials. Composite is a combination of two or more elements that get combined properties of the elements combined. Liquid Epoxy resin is a low molecular weight organic group containing epoxide. The composite material used is a fiber reinforced resin nut shell. Point of this study is know tensile strength of fiber nut shell composite, variations in the composition of the epoxy resin and fiber nut shell made in this study was 90:10%wt, 80:20%wt, and 70:30%wt, fiber length of 2 cm with random fiber orientation. This experiment is the tensile test. Tensile test was conducted to determine the tensile stress each - each composition, the standard used is ASTM 638 02. From the test results obtained on the composition of the composite tensile strength of 90: 10% wt is 9.8 MPa, the composition of 80: 20% wt was 13.06 MPa and the composition of 70: 30% wt is 14.04 MPa. Of the fracture surface can be seen that the fibers are well distributed and the bond between resin and fiber is also more evenly so that the tensile strength increased.
Referensi
M. M. Schwartz (1984). “Material Komposit Handbook”. McGraw-Hill, New York, Amerika Serikat.
K.G. Budinski (2003). “Engineering Material Properties and Selection“. Prentice Hall, New Jersey.
R. Ruslinda (2008). “Kandungan Serat Buah Pinang“. ITB, Bandung.
B. Agustinus, S. Rudy dan A.S. Achmad (2014 ), “Analisa Persentase Alkali pada Serat Pangkal Pelepah Daun Pinang ( Areca Catechu ) terhadap Sifat Mekanis Komposit Polimer“. Universitas Brawijaya, Malang.
Joni, L. Johannes dan S. Rafiuddin (2008), “Analisis Kekuatan Tarik dan Lentur Komposit Epoksi yang Diperkuat Serat Kulit Kayu Khombow”.
A.J., Hartomo. (1992). “Polimer dan Perekat “. Yogyakarta
D.R. Askeland, (1985). “The Science and Engineering of Material “. Alternate Edition, PWS Engineering, Boston.
P. N. Belaguru annd S. P. Shah (1992). “Fiber-reinforced Concrete Composites “. McGraw-Hill, New York.
D. Feldman dan A. J. Hartomo (1995). “Bahan Polimer Konstruksi Bangunan “. PT. Gramedia Pustaka Utama, Jakarta.
H. Fahmi, Hendriwan (2011). “Pengaruh Orientasi Serat Pada Komposit Resin Polyester / Serat Daun Nenas Terhadap Kekuatan Tarik “. ITP. Padang.
R. F. Gibson, (1994). “Principles of Composite Material Mechanics “. McGraw-Hill Inc., St. Louis.
Hendrodiyantopo (1998). “Teknik Penyempurnaan “. STTT, Bandung.
A. K. Kaw, (2006). “Mechanics of Composites Materials “. Taylor & Francis Group, New York.
M. Kumar (2008). “A study of Short Areca Fiber Reinforced PF Composites”. WCE, London, U.K.
D. Kuncoro (2006). “Pengaruh Perlakuan Alkali terhadap Sifat Tarik Bahan Komposit Serat Rami-Polyester “. Jurnal Teknik Mesin Vol. 8 No.1.
T. Richardson (1987). “Composites“. Industrial Press Inc., New York.
M. M. Schwartz (1992). “Material Komposit Handbook: 2nded “. McGraw-Hill Inc., New Jersey
B. Srinivasa (2013). “Effect of Alkali Treatment On Impact Bahavior of Areca Fibers Reinforced Polymer Composites”. International Journal of Chemical, Molecular, Nuclear, Materials, and Metallurgical Engineering,
T. Surdia (1985). “ Pengetahuan Bahan Teknik “. Jakarta.
R. Wulandari, (2009). “Komposit Polypropylene: Fashion Baru Dalam Otomatif “. Sentra Polimer tahun VIII Nomor 29. Sentra Teknologi Polimer, Tangerang.
Unduhan
Diterbitkan
Terbitan
Bagian
Lisensi
Artikel ini berlisensiCreative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.