ANALISA STRUKTUR MIKRO LAPISAN KROM DAN NIKEL PADA BAHAN DASAR KUNINGAN
DOI:
https://doi.org/10.21063/jtm.2015.v5.i1.12-17Kata Kunci:
Elektroplating, nickel, chrome, adhesivitas, currentAbstrak
Chrome elektroplating in metal product is a way to increase the value of metal industial doer especially home industry. The best elektroplating can be shown in adhesion stratum in the metal, stratum shine, stratum thick, and substance of the stratum. Chrome elektroplating in a basic metal was done by two steps. First, nickel elektroplating and second, chrome elektroplating. Nickel elektroplating was done in current 3.5 Ampere, 9 Ampere, and 11 Ampere in twenty minutes. Both nickel and chrome elektroplating was done by dip method and current source from battery. Based on experimental data and the discussion, it can be perpoker substance, the thick of chrome elektroplating is 1 μm, 1.5 μm, 2.3 μm for current application 7 Ampere, 9 Ampere, and 11 Ampere solution. Coating adhesion and shiny of metal is good.
Referensi
Abrams, H., 1971. “Grain Size Measurement by the Intercept Method,” Metallography, Vol. 4, , pp. 59–78.
Asfarizal, Nurzal, 2013. Crome Plating to Increase the added value of Home Industry Metal Product West Sumatra Jurnal teknik mesin-itp vol.3 no. 2 tahun Oktober hal 55-59.
Asfarizal dan Yusnadi., 2011. Pengaruh Waktu Listrik Terhadap Kualitas Lapisan Khrom Pada Baja Karbon Rendah, Jurnal Momentum Vol.11, No.2, Hal 5-13.ITP.
Adyani, I.A.S., 2009., Pengaruh Kuat Arus Terhadap Ketebalan dan Kekerasan Lapisan Khrom Pada Stoneware dan Earthenware, Jurnal Teknologi Elektro Vol. 8 No. 2 Juli-Desember 2009, Mataram. [5] Canning, 1982.,The Canning Handbook, Surface Finishing Technology.
Hartomo, A.J. dan Kaneko, T., 1995, Mengenal pelapisan logam (electro plating), Andi offset, Yogyakarta
Juandi, S., 2014, Pelapisan Listrik Tembaga Terhadap Plat Baja Dengan Larutan Asam Tembaga, Padang.
Saleh, A.A., 1995, Pelapisan Logam, Buku Pegangan Industry Elektroplating, Balai Besar Pengembangan Industri Logam dan Mesin, Bandung.
Vander Voort, G. F., “Grain Size Measurement,” Practical Applications of Quantitative Metallography, ASTM STP 839, 1984, pp. 85-181.
Yogik Dwi Mustopo., 2011. Pengaruh Waktu Terhadap Ketebalan dan Adhesivitas Lapisan pada Proses Elektroplating Khrom Dekoratif Tanpa Lapisan Dasar, Dengan Lapisan Dasar Tembaga dan Tembaga-Nikel, Universitas Sebelas Maret, Surakarta.
Unduhan
Diterbitkan
Terbitan
Bagian
Lisensi
Artikel ini berlisensiCreative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.